Tables of Material Data

Table 2: Material Data
Table 2: Material Data
Table 2: Material Data
  • Column 2: The sealing metals indicated are described in table 3.
  • Column 3: a 20-300: Mean linear coefficient of expansion in the temperature range from 20 to 300°C according to DIN 52 328.
  • Column 4: Tg: Transformation temperature according to DIN 52 324
  • Column 5: Viscosity: The indicated viscosity temperatures mark the following processing stages.
    107.6 dPas (softening temperature): Noticeable deformation of glasses under their own weight, even after short heating periods (minutes).
    104 (processing temperature): Central viscosity of the range from 103 to 105 dPas in which most processing techniques such as pressing, blowing and drawing are applied.
  • Column 7: tk100 value: Temperature at which the electrical resistivity is 108 W cm according to DIN 52 326.
  • Column 9: DZ: Dielectric constant; tan d: Dissipation factor.
  • Column 10: W: Resistance to water according to DIN ISO 719
    S: Resistance to acid according to DIN 12 116
    L: Resistance to alkaline solutions according to DIN ISO 695
    W is subdivided into 5 resistance classes, S into 4 and L into 3. The higher the class number, the lower the resistance.
Table 3: Sealing Metals
Table 3: Sealing Metals
Table 3: Sealing Metals
Exhibitions & Events
13.
March
Exhibition OFC 2018, San Diego, CA, USA, 03-13 to 03-15-2018
17.
September
Exhibition Gastech, Barcelona, Spain, 09-17 to 09-20-2018
13.
November
Exhibition electronica, Munich, Germany, 11-13 to 11-16-2018
Contact
Electronic Packaging
SCHOTT North America, Inc.

15 Wells Street
Southbridge, MA 01550
USA
E-Mail to SCHOTT+1 (508) 765-7450
SCHOTT uses Cookies on this Website to enhance the user experience and provide the best possible Service. By continuing to browse the Website, you consent to our use of Cookies.