S8612
- SCHOTT
- S8612 - S8612
- 厚度
- 1.0
- 反射系数
- 0.9135
λ [nm] | |
---|---|
200 | < 10⁻³ |
210 | < 10⁻³ |
220 | < 10⁻³ |
230 | < 10⁻³ |
240 | < 10⁻³ |
250 | < 10⁻³ |
260 | < 10⁻³ |
270 | < 10⁻³ |
280 | < 10⁻³ |
290 | < 10⁻³ |
300 | 0.001 |
310 | 0.070 |
320 | 0.326 |
330 | 0.584 |
340 | 0.732 |
350 | 0.805 |
360 | 0.847 |
370 | 0.872 |
380 | 0.894 |
390 | 0.910 |
400 | 0.924 |
410 | 0.935 |
420 | 0.945 |
430 | 0.954 |
440 | 0.961 |
450 | 0.967 |
460 | 0.972 |
470 | 0.976 |
480 | 0.980 |
490 | 0.981 |
λ [nm] | |
---|---|
500 | 0.981 |
510 | 0.979 |
520 | 0.971 |
530 | 0.958 |
540 | 0.938 |
550 | 0.906 |
560 | 0.863 |
570 | 0.803 |
580 | 0.728 |
590 | 0.638 |
600 | 0.539 |
610 | 0.438 |
620 | 0.340 |
630 | 0.253 |
640 | 0.181 |
650 | 0.123 |
660 | 0.080 |
670 | 0.050 |
680 | 0.030 |
690 | 0.017 |
700 | 0.010 |
710 | 0.005 |
720 | 0.003 |
730 | 0.002 |
740 | < 10⁻³ |
750 | < 10⁻³ |
760 | < 10⁻³ |
770 | < 10⁻³ |
780 | < 10⁻³ |
790 | < 10⁻³ |
λ [nm] | |
---|---|
800 | < 10⁻³ |
810 | < 10⁻³ |
820 | < 10⁻³ |
830 | < 10⁻³ |
840 | < 10⁻³ |
850 | < 10⁻³ |
860 | < 10⁻³ |
870 | < 10⁻³ |
880 | < 10⁻³ |
890 | < 10⁻³ |
900 | < 10⁻³ |
910 | < 10⁻³ |
920 | < 10⁻³ |
930 | < 10⁻³ |
940 | < 10⁻³ |
950 | < 10⁻³ |
960 | < 10⁻³ |
970 | < 10⁻³ |
980 | < 10⁻³ |
990 | < 10⁻³ |
1,000 | < 10⁻³ |
1,010 | < 10⁻³ |
1,020 | < 10⁻³ |
1,030 | < 10⁻³ |
1,040 | < 10⁻³ |
1,050 | < 10⁻³ |
1,060 | < 10⁻³ |
1,070 | < 10⁻³ |
1,080 | < 10⁻³ |
1,090 | < 10⁻³ |
λ [nm] | |
---|---|
1,100 | < 10⁻³ |
1,110 | < 10⁻³ |
1,120 | < 10⁻³ |
1,130 | < 10⁻³ |
1,140 | < 10⁻³ |
1,150 | 0.001 |
1,160 | 0.001 |
1,170 | 0.002 |
1,180 | 0.002 |
1,190 | 0.002 |
1,200 | 0.003 |
1,250 | 0.007 |
1,300 | 0.017 |
1,350 | 0.035 |
1,400 | 0.063 |
1,450 | 0.106 |
1,500 | 0.163 |
1,550 | 0.233 |
1,600 | 0.311 |
1,650 | 0.391 |
1,700 | 0.467 |
1,750 | 0.538 |
1,800 | 0.601 |
1,850 | 0.656 |
1,900 | 0.702 |
1,950 | 0.740 |
2,000 | 0.770 |
2,050 | 0.793 |
2,100 | 0.811 |
2,150 | 0.825 |
λ [nm] | |
---|---|
2,200 | 0.821 |
2,250 | 0.818 |
2,300 | 0.819 |
2,350 | 0.823 |
2,400 | 0.826 |
2,450 | 0.823 |
2,500 | 0.809 |
2,550 | 0.783 |
2,600 | 0.757 |
2,650 | 0.735 |
2,700 | 0.697 |
2,750 | 0.622 |
2,800 | 0.307 |
2,850 | 0.143 |
2,900 | 0.082 |
2,950 | 0.053 |
3,000 | 0.037 |
3,050 | 0.027 |
3,100 | 0.019 |
3,150 | 0.014 |
3,200 | 0.011 |
3,250 | 0.009 |
3,300 | 0.007 |
3,350 | 0.007 |
3,400 | 0.006 |
3,450 | 0.007 |
3,500 | 0.007 |
3,550 | 0.008 |
3,600 | 0.009 |
3,650 | 0.010 |
λ [nm] | |
---|---|
3,700 | 0.011 |
3,750 | 0.010 |
3,800 | 0.009 |
3,850 | 0.008 |
3,900 | 0.006 |
3,950 | 0.004 |
4,000 | 0.003 |
4,050 | 0.002 |
4,100 | 0.001 |
4,150 | < 10⁻³ |
4,200 | < 10⁻³ |
4,250 | < 10⁻³ |
4,300 | < 10⁻³ |
4,350 | 0.001 |
4,400 | 0.001 |
4,450 | 0.002 |
4,500 | 0.001 |
4,550 | 0.001 |
4,600 | 0.001 |
4,650 | 0.001 |
4,700 | < 10⁻³ |
4,750 | < 10⁻³ |
4,800 | < 10⁻³ |
4,850 | < 10⁻³ |
4,900 | < 10⁻³ |
4,950 | < 10⁻³ |
5,000 | < 10⁻³ |
5,050 | < 10⁻³ |
5,100 | < 10⁻³ |
5,150 | < 10⁻³ |
反射系数 | |
---|---|
Pd | 0.913 |
参考厚度 | |
---|---|
d [mm] | 1 |
承诺光谱值 | |
---|---|
τi (500nm) | ≥0.96 |
τi (600nm) | ≥0.48 |
τi (700nm) | <0.02 |
λ (τi, max) [nm] | 500± 5 |
折射率 n |
---|
nF (486.1 nm) = 1.546 |
nh (404.7 nm) = 1.554 |
ng (435.8 nm) = 1.550 |
ns (852.1 nm) = 1.533 |
ne (546.1 nm) = 1.542 |
nd (587.6 nm) = 1.540 |
色度评估
光源 | A(Planck T = 2347K) | ||
---|---|---|---|
d [mm] | 1 | 2 | 3 |
x | 0.356 | 0.301 | 0.265 |
y | 0.433 | 0.440 | 0.440 |
Y | 65 | 52 | 44 |
λd [nm] | 500 | 499 | 498 |
Pe | 0.21 | 0.34 | 0.42 |
光源 | Planck T = 3200 K | ||
---|---|---|---|
d [mm] | 1 | 2 | 3 |
x | 0.335 | 0.284 | 0.250 |
y | 0.417 | 0.419 | 0.415 |
Y | 66 | 54 | 46 |
λd [nm] | 498 | 497 | 496 |
Pe | 0.21 | 0.34 | 0.43 |
光源 | D65 (TC = 6504 K) | ||
---|---|---|---|
d [mm] | 1 | 2 | 3 |
x | 0.251 | 0.218 | 0.198 |
y | 0.321 | 0.311 | 0.302 |
Y | 72 | 62 | 54 |
λd [nm] | 490 | 489 | 489 |
Pe | 0.23 | 0.36 | 0.44 |
密度 | |
---|---|
p [g/cm3] | 2.66 |
气泡含量 | |
---|---|
气泡等级 |
玻转温度 | |
---|---|
Tg [°C] | 391 |
温度系数 | |
---|---|
Tk [nm/°C] |
耐化学性 | |
---|---|
耐污性 | 0 |
耐酸性 | 3.0 |
耐碱性 | 3.0 |
热膨胀 | |
---|---|
α-30°C/+70°C [10-6/K] | |
α20°C/300°C [10-6/K] | 9.5 |
α20°C/200°C [10-6/K] |